E603 Non Skid Epoxy | Truck Bed Liner | Anti-Slip

Chemical Resistance, Splash & Spillage 

• Beer
• Calcium Chloride
• Citric Acid 10%
• Cutting Oil
• Diesel FUel
• Fish Oil
• Gasoline
• Hydraulic Fluid
• Jet Fuel
• Kerosene
• Lactic Acid 20%
• Lard
• Mineral Sprits
• Motor Oil
• Olive Oil
• Phosphoric Acid 20%
• Sodium Hydroxide 25%
• Wine

COVERAGE RATE

                                                              CURE TIME

REGULAR CURE                                           

Temperature                           Light Traffic                      Heavy Traffic                   

90ºF                                  18 hours                              48 hours

75ºF                                  24 hours                               72 hours

50ºF                                  36 hours                                96 hours

For safety and proper product curing, good ventilation is necessary when painting indoors or in confined areas.  Be sure the batch numbers are all the same to provide uniform color.  Epoxy coatings may yellow or darken during application and after final cure.  This will affect the color but will have no effect on the performance of the product.  Heaters that emit carbon dioxide and carbon monoxide can cause the coating to yellow.

MIXING AND APPLICATION INSTRUCTIONS

SURFACE PREPARATION

Concrete 

In all cases of surface preparation, the pH should be checked. A pH reading of 7.0 to 8.5 is acceptable. Also, a Water Dissipation Test should be made on random areas of the floor to determine if the proper degree of porosity has been achieved. Before the installation of any Paint Products, the substrate should be examined for moisture. Test for moisture vapor transmission using ASTM F-1869 Standard Test Method for Measuring Moisture Vapor Emission Rate of Concrete Subfloor using Anhydrous Calcium Chloride. The maximum allowable rate is 3lbs per 1,000 square feet per 24 hours. Test for relative humidity in concrete floor slabs using Probes according to ASTM F-2170. This test measures the presence relative humidity of the slab below the surface. The maximum relative humidity should be below 80%.

New concrete must be cured at least a minimum of 28 days before applying a coating.  On-grade slabs must have moisture vapor barrier in place.  All laitance, sealers, efflorescence, chemical contaminants, grease, oil and other foreign material must be removed.  The prepared surface must be clean, dry and structurally sound.  We recommends mechanical preparation by means of shot blasting or diamond grinding to achieve a CSP-2 or CSP-3 profile, in accordance with the International Concrete Repair Institute (ICRI).  The profile should reflect something similar to a 60 -100 grit sandpaper.  If the substrate is not properly prepared and the appropriate profile is not achieved, failure of the product to adhere to the substrate may occur.

Old concrete surfaces must be structurally sound.  Any unsound areas must be repaired prior to proceeding with the resinous installation.  For proper patching and repairing, use E615 Epoxy Crack Filler and/or E1000 Epoxy Concrete Repair Kit  with graded aggregate.  Remove existing paint and loose concrete by rough sanding, sandblasting, high pressure water cleaning, shot blasting or grinding.  In some cases where plant conditions allow, a stripper may be used to remove excessive build-up of paints or sealers.

Steel

Remove all dirt, grease, oil, soil, chemical contaminants and other matter before any mechanical preparation.  The surface must be free of any salt contamination.  Prepare and paint only clean surfaces in accordance with Steel Structures Painting Council (SSPC) or National Association of Corrosion Engineers (N.A.C.E.) specifications.

1. Sand Blast – Best

Sand Blast to a “Commercial” (SSPC-SP6) or “Near White” (SSPC-SP10) metal finish.

1. Power Tool Clean

Follow instructions as outlined in SSPC-SP3 specification.

Prime the same day with E15 Epoxy Mastic.

MIXING INSTRUCTIONS

E603 is prepared by mixing 4 parts Base (Part A) to 1 part Hardener (Part B) with a 400-600 RPM explosion proof variable speed drill and Jiffy mixer.  Use immediately after mixing, no induction time is needed.

APPLICATION PROCEDURE

Do not apply until surface has been properly prepared.  For best results, prime concrete with  E155 Concrete Primer.  On steel surfaces, prime with E15 Epoxy Mastic.  Allow primer to cure before applying E603. E603 should be applied with a honeycomb roller cover or shed resistant roller cover. Immediately after mixing, pour a ribbon of E603 on to surface.  Do not over roll material this can decrease the non-skid.  Roll material only in one direction.  Strike off any excessive material build-up on edges from roller lap.  The spread rate is approximately 120-180 sq. ft. per gallon.  Do not apply over expansion joints.  Do not apply if the surface temperature is within 5° of the dew point.  Always apply a test patch of E603 for owners approval prior to application.

CAUTIONS

E603 Base is flammable.  E603 Hardener is corrosive.  Keep away from all sources of ignition during mixing, application and cure.  The HARDENER and BASE can cause eye and skin burns as well as allergic reactions.   The use of goggles, fresh air masks or NIOSH approved respirators, protective skin cream and protective clothing. This product is sold without warranty as to performance expressed or implied.  Users are urged to make their own tests to determine the suitability for their particular conditions.

SEE SAFETY DATA SHEET FOR FULL SAFETY PRECAUTIONS. KEEP AWAY FROM CHILDREN. NOT FOR RESIDENTIAL USE. FOR PROFESSIONAL AND INDUSTRIAL USE ONLY.

SEE MATERIAL SAFETY DATA SHEET FOR FULL SAFETY PRECAUTIONS.  FOR PROFESSIONAL AND INDUSTRIAL USE ONLY  KEEP AWAY FROM CHILDREN.  NOT FOR RESIDENTIAL USE NOTICE TO BUYER: DISCLAIMER OF WARRANTIES AND LIMITATIONS ON OUR LIABILITY We warrant that our products are manufactured to strict quality assurance specifications and that the information supplied by us is accurate to the best of our knowledge. Such information supplied about our products is not a representation or a warranty. It is supplied on the condition that you shall make your own tests to determine the suitability of our product for your particular purpose. Any use or application other than recommended herein is the sole responsibility of the user. Listed physical properties are typical and should not be construed as specifications. NO WARRANTY IS MADE, EXPRESSED OR IMPLIED, REGARDING SUCH OTHER INFORMATION, THE DATA ON WHICH IT IS BASED, OR THE RESULTS YOU WILL OBTAIN FROM ITS USE. N0 WARRANTY IS MADE, EXPRESSED OR IMPLIED, THAT OUR PRODUCT SHALL BE MERCHANTABLE OR THAT OUR PRODUCT SHALL BE FIT FOR ANY PARTICULAR PURPOSE. NO WARRANTY IS MADE THAT THE USE OF SUCH INFORMATION OR OUR PRODUCT WILL NOT INFRINGE UPON ANY PATENT. We shall have no liability for incidental or consequential damages, direct or indirect. Our liability is limited to the net selling price of our product or the replacement of our product, at our option. Acceptance of delivery of our product means that you have accepted the terms of this warranty whether or not purchase orders or other documents state terms that vary from this warranty. No representative is authorized to make any representation or warranty or assume any other liability on our behalf with any sale of our products. Our products contain chemicals that may CAUSE SERIOUS PHYSICAL INJURY. BEFORE USING, READ THE SAFETY DATA SHEET AND FOLLOW THE PRECAUTIONS TO PREVENT BODILY HARM.