E126CW Cold Weather Epoxy Mortar Concrete Resurfacer & Patch

E126CW is a premium cold temperature high performance three component 100% solids epoxy mortar designed for patching or resurfacing concrete floor applications where excellent durability and wear characteristics are required.

Designed for use in cold storage applications and for cold temperate outdoor use during the fall and winter months.    Recommended for resurfacing and repair of concrete floors, cold storage, walkways, loading docks, seamless floors and general patching.  Designed for resurfacing from 1/8″ to 1/4″ and patching up to 2″ deep.

The E126CW offers is extremely durable, resistant to wear and tear, and good chemical resistance.  The E126CW is typically used to resurface older, damaged concrete.   Epoxy Mortar products offer higher impact resistance and greater compressive strength than typical concrete.

The E126CW is available in 5  colors: light gray, dark gray, black, tile red, natural and comes packaged in 4 sizes which includes liquid Parts A and B plus aggregate.  1 unit (0.45 cubic feet) of E126CW has a coverage rate of 21.45 sq’ @1/4″ and 43.1 sq’ @1/8″ and comes with 9 lbs Part A, 2.2 lbs Part B and 50 lbs of aggregate. E126CW also is available 1/4 units (0.11 cubic feet), 1/2 units (0.22 cubic feet) and a bulk (5) unit size (2.25 cubic feet)

Application temperature range 35°F to 80°F.

PRIMER: No primer is necessary. This material is self-priming. However, any suitable primer can be used.

TOPCOAT: None recommended. Many epoxies, polyaspartics and urethanes can be used

 Where is the E126CW Epoxy Mortar/Patch Used?

  • Cold Storage & Freezer Areas
  • Garages
  • Warehouses
  • Loading docks
  • Walkways
  • Manufacturing plants

Why E126CW Epoxy Mortar/Patch?

  • Great for Cold Weather & Cold Freezer Storage
  • Easy resurfacing old and damaged concrete floors
  • Premium Tough, Durable, Chemical Resistant Protection
  • Compressive Strength 11,284 psi ASTM D695
  • Heat Deflection Temp 149.9F ASTM D648
  • High Build Resurfacing 1/8″ to 1/4″
  • Patching up to 2″ thick
  • 100% solids epoxy
  • Application range 35°F to 80°F
  • Comes complete with epoxy and aggregate
  • Selection of 5 color options

SPECIFICATIONS

Solids By Weight 100%   By Volume 100%
VOC 0 g/L
Colors light gray, dark gray, red, natural, black
Recommended Film Thickness 1/8″ to 1/4″
Coverage per Gallon 1 Unit 21.54 sq’ @ 1/4″ and 43.1 sq’ #1/8″
Packaging 1/4 unit 0.11 cubic feet, 1 unit 0.45 cubic feet, bulk unit 2.25 cubic feet
Mix Ratio (mix ratio) .84-.86 gallons part A to .28 gallons part B
Shelf Life 2 years in unopened container
Weathering good (chalks)
Abrasion Resistance Excellent
Flexural strength 11,754 psi@ ASTM D790-
Compressive strength 11,150 psi @ASTM D695
Tensile strength 7,749 psi @ ASTM D638
Ultimate Elongation 4.8%
Viscosity Part A 950-1,250 cps, Part B 700-900 cps
Heat Deflection Temp 149.8 degrees F @ASTM D-648

Coverage Rate

Coverage Per Gallon 1 Unit 21.54 Sq’ @ 1/4″ And 43.1 Sq’ #1/8″

CURE SCHEDULE

Pot Life – (0.45 cubic feet volume) 20-30 minutes
Recoat or topcoat 4 – 5 hours
Light foot traffic 10-12 hours
Full cure (heavy traffic) 2-7 days

APPLICATION TEMPERATURE: 35-80 degrees F with relative humidity below 90%

CHEMICAL RESISTANCE

RATING
 Xylene B
 1.1.1 trichlorethane A
MEK A
Ethyl Alcohol B
Skydrol B
 10% sodium hydroxide E
 50% sodium hydroxide D
 10% sulfuric Acid C
70% Sulfuric Acid A
10% HCI B
5% acetic acid A

Rating key: A – not recommended, B – 2 hour term splash spill, C – 8 hour term splash spill, D – 72 hour immersion, E – long term immersion.

MIXING AND APPLICATION INSTRUCTIONS

RODUCT STORAGE: Store product in an area so as to bring the material room temperature before using. : Store product in an area so as to bring the material to normal room temperature before using.  Continuous storage should be above 55 degree F to prevent product crystallization.

SURFACE PREPARATION: All dirt, oil, dust, foreign contaminants and laitance must be removed to assure a trouble free bond to the substrate. We recommend that an aggressive shot blast be performed prior to the application of this product.  A less adequate method would be acid etching, but the etching should properly profile the substrate. All edges and around columns or beams should be mechanically scarified. All termination points should not be feather edged, but should be saw cut with the termination ending at the sawcut. All large cracks should be V cut and filled with appropriate crack filler.

All expansion joints should be filled with appropriate joint filler.   When overlaying an expansion joint, a single saw cut through the epoxy overlay will prevent random fracturing.

A test should be made to determine that the concrete is dry; this can be done by placing a 4’x4′ plastic sheet on the substrate and taping down the edges; if after 24 hours, the substrate is still dry below the plastic sheet, then the substrate is dry enough to start coating. The plastic sheet testing is also a good method to determine if any hydrostatic pressure problems exist that may later cause disbonding

PRODUCT MIXING: It is important that the liquids be mixed together first. Mix the liquids in an oversized container thoroughly and until streak free. After the liquids are thoroughly mixed, add in the aggregate. Mix in the aggregate with slow speed mixing equipment such as a jiffy mixer or rotating bucket/stationary mixing blade assembly. It is equally important that enough time is spent mixing in the aggregate to insure that the aggregate is thoroughly wetted out. No induction time is necessary. Improper mixing may result in product failure. This material has a high viscosity – mix well.

Improper mixing may result in product failure. For best mixing results and proper blending of parts A and B, recommend a Jiffy Mixer style drill mixer.

Use of an improper drill mixer can result in streaking of the color because the pigment has not been thoroughly blended.  It can also create curing problems if the hardener also called activator (Part B) is not thoroughly blended with the resin (Part A) which can cause some areas on your floor to remain soft and not harden properly.  DO NOT USE A PAINT MIXER.  Many mixing problems described above can be traced back to using a paint mixer..  DO NOT HAND MIX as this approach can also result in the same problems as using a paint mixer.

PRIMING: No primer is necessary. This material is self-priming. However, any suitable primer can be used.

PRODUCT APPLICATION: Apply the mixed material at 1/8 to 1/4 inch thickness. Apply the material with a hand trowel or other suitable application equipment. Maintain temperatures within the recommended ranges during the application and curing process. Do not over-trowel the mortar as this can cause blistering. Air currents directly across or above the mortar may also cause blistering.

RECOAT OR TOPCOATING: No recoating or topcoating is necessary. However, if you opt to topcoat the applied mortar, allow it to cure before topcoating. Many epoxies and urethanes can be used.

CLEANUP: Use xylol.

FLOOR CLEANING: Caution!  Some cleaners may affect the color of the floor installed. Test each cleaner in a small area, utilizing your cleaning technique.  If no ill effects are noted, you can continue to clean with the product and process tested.

RESTRICTIONS: Restrict the use of the floor to light traffic and non-harsh chemicals until the coating is fully cured (see technical data under full cure).  It is best to let the floor remain dry for the full cure cycle. Dependent on actual complete system application, surface may be slippery, especially when wet or contaminated; keep surface clean and dry.

LIMITATIONS:

  • Color stability or gloss may be affected by environmental conditions such as high humidity, low temperature or chemical exposure.
  • Colors may vary from batch to batch. Therefore, use only product from the same batch for an entire job.
  • This product is not UV color stable and exposure to lighting such as sodium vapor lights may cause discolorations.
  • For chemical exposure areas, we recommend a suitable topcoat to reduce porosity and chemical migration.
  • Substrate temperature must be 5°F above dew point.
  • All new concrete must be cured for at least 30 days prior to application.
  • Physical properties are typical values and not specifications.

NOTICE TO BUYER: DISCLAIMER OF WARRANTIES AND LIMITATIONS ON OUR LIABILITY We warrant that our products are manufactured to strict quality assurance specifications and that the information supplied by us is accurate to the best of our knowledge. Such information supplied about our products is not a representation or a warranty. It is supplied on the condition that you shall make your own tests to determine the suitability of our product for your particular purpose. Any use or application other than recommended herein is the sole responsibility of the user. Listed physical properties are typical and should not be construed as specifications. NO WARRANTY IS MADE, EXPRESSED OR IMPLIED, REGARDING SUCH OTHER INFORMATION, THE DATA ON WHICH IT IS BASED, OR THE RESULTS YOU WILL OBTAIN FROM ITS USE. N0 WARRANTY IS MADE, EXPRESSED OR IMPLIED, THAT OUR PRODUCT SHALL BE MERCHANTABLE OR THAT OUR PRODUCT SHALL BE FIT FOR ANY PARTICULAR PURPOSE. NO WARRANTY IS MADE THAT THE USE OF SUCH INFORMATION OR OUR PRODUCT WILL NOT INFRINGE UPON ANY PATENT. We shall have no liability for incidental or consequential damages, direct or indirect. Our liability is limited to the net selling price of our product or the replacement of our product, at our option. Acceptance of delivery of our product means that you have accepted the terms of this warranty whether or not purchase orders or other documents state terms that vary from this warranty. No representative is authorized to make any representation or warranty or assume any other liability on our behalf with any sale of our products. Our products contain chemicals that may CAUSE SERIOUS PHYSICAL INJURY. BEFORE USING, READ THE SAFETY DATA SHEET AND FOLLOW THE PRECAUTIONS TO PREVENT BODILY HARM.